軟磁合金量測

 

Magneization Curves of Soft Magnetic Materials for DC Hysteresis

 

收案樣本涵蓋  高導磁合金、純鐵、鎳鋅 Ni-Zn、濾波器EMI、高電感磁芯、其他低矯頑磁力材料

 

1. 客戶提交預計量測的軟磁樣本,樣本可以接受為中空環狀的圓柱體,同時請提供樣本的材証及密度資料。

Customer provide the soft magnetic sample that is expected to be measured. The sample can be accepted as a hollow circular cylinder. Please also provide the material and density data of the sample.

 

軟磁量測樣本需求

 

 

2.  告知預計想要量測的項目,如Br、Hc、Bmax、Hmax、permeability、等資料。若無特別要求則依照一般流程進行四象限的磁滯分析。

Inform the project that you want to measure, such as Br, Hc, Bmax, Hmax, durability, and more. If there is no special requirement, follow the general procedure as hysteresis analysis of four quadrants.

 

3.  提供的樣本必須告知是否已經有進行熱處理? 是否為原材或者經過後加工製程

The sample provided must inform whether it has been heat treatment? Whether it is a raw material or a post-processing process

 

4. 出具正式的磁滯曲線報告乙份 (B-H Curve)

Issue a formal B-H Curve report



 

軟磁合金在低磁場中可以得到較高的導磁率及低矯頑力的特性,而要獲得較高的磁性能數據則有賴於熱處理的工藝。進行退火時原子開始受熱振動而使得晶格開始鬆動,超過居禮溫度時自發磁化消失,由鐵磁性轉變為順磁性。高溫時晶粒成長,晶隙變小,缺陷降低。當合金退火到居禮溫度時發生磁性轉變,合金中的磁疇受自發磁性的影響進而從順磁性轉變為鐵磁性。緩慢冷卻時亦發生有序化轉變,原子按一定方向排列,增加磁性能,飽和磁通提高。

 

高溫下氫氣將與金屬表面雜質產生化學反應,可有效淨化合金表面,表面殘留雜值減少,這是因為氫還原能力高所致。熱處理過程使得軟磁合金消除內應力,晶粒均勻成長,獲得良好的磁性能。而進一步量測磁性能則根據法規ASTM A773及IEC 60404-4進行DC磁性能量測。封閉磁路中使用標準樣本測量軟磁材料的直流磁性能,一般環形樣本建議適用於磁場強度在125 Oe以下的測量。

 

B-H loop 曲線報告

 

 